T700 12K kain serat karbon 300g searah
T700 12K kain serat karbon 300g searah
T700 12K kain serat karbon 300g searah
T700 12K kain serat karbon 300g searah
T700 12K kain serat karbon 300g searah
T700 12K kain serat karbon 300g searah
T700 12K kain serat karbon 300g searah
T700 12K kain serat karbon 300g searah

T700 12K kain serat karbon 300g searah

$16.19100-499 Others

$13.97500-999 Others

$13.73≥1000Others

Jenis pembayaran:L/C,Western Union,T/T
Inkoterm:FOB,CFR,CIF,EXW,Express Delivery
Transportasi:Ocean,Land,Air,Express
Pelabuhan:All ports in China
Color:
Atribut Produk

Model NoTJ-029

MerekPhecda

TechnicsWoven

Product TypeCarbon Fiber Fabric

Width0.5m, 100-1000mm

PatternSolids

Supply TypeMake-To-Order

Material100% Carbon Fiber

FeatureAbrasion-Resistant, Anti-Static, Heat-Insulation, DIMENSIONAL, QUICK-DRY, against earthquake, High temperature resistance,acid base corrosion resistance

UseIndustry

Model NumberH12K-CF300(500mm wide)

Applicable To The CrowdWomen, Men

Yarn GradeI

Tensile Strength(Mpa)≥3500

Tensile Modulus(Gpa)≥240

Elongation≥1.7

ColorBlack

Place Of OriginChina

StyleUnidirectional

Weight300g/m2

Ketebalanlightweight, 0.167mm

Place Of OriginJiangsu, China

Brand NamePHECDA

& pengiriman paket
Menjual unit : square meter
Tipe paket : karton atau oleh klien diperlukan

The file is encrypted. Please fill in the following information to continue accessing it

T700 12K Fabric serat karbon 300g searah untuk penguatan bangunan1
Kain serat karbon 12k searah1
Deskripsi Produk



12k kain serat karbon ud

12K Polimer Bertulang Serat Karbon 12K (UD-CFRP) tidak memiliki modulus elastisitas dan kekuatan dalam arah lateral. Studi ini menyelidiki apakah resin matriks dengan limbah CFRP, daur ulang serat karbon (RCF), dapat meningkatkan sifat lateral CFRP. Secara total, dua belas spesimen strip CFRP adalah prefabrikasi dari lembaran serat karbon unidirectional (CF) dengan lapisan tangan (HLU) dan diuji dengan uji tarik dan tomografi terkomputasi sinar-X (X-ray CT). Faktor-faktor seperti arah serat dan distribusi batal secara signifikan mempengaruhi sifat mekaniknya dinilai dengan inspeksi CT sinar-X. Dapat dilihat bahwa RCF dicampur dalam arah acak pada posisi yang diisi dengan resin matriks tanpa RCF. Namun, frekuensi serupa dari tidak terimpregnasi dan rongga dapat diamati pada kedua spesimen. Hasil tes menunjukkan bahwa nilai-nilai eksperimental laminasi CFRP dengan resin matriks-campuran-rcf meningkat dibandingkan dengan laminasi CFRP tanpa RCF. Persentase peningkatan kekuatan tarik lateral dan modulus elastisitas RCFRP dibandingkan dengan spesimen kontrol tanpa RCF masing -masing adalah 27,36% dan 10,62%. Ini membuktikan bahwa RCF dapat meningkatkan sifat lateral CFRP searah dan menunjukkan penggunaan RCF yang efektif untuk memperkuat bahan dalam aplikasi konstruksi.






12K Carbon Fiber Fabric
Unidirectional 300g Carbon Fiber Fabric
Type
Grade
Tensile Strength(Mpa)
Tensile Modulus(Gpa)
Elongation(%)
Thickness(mm)
Weight(g/㎡)
H12K-CF200
I
≥3500
≥240
≥1.7
0.111
200

II
≥3200
≥210
≥1.5
0.111
200
H12K-CF300
I
≥3500
≥240
≥1.7
0.167
300

II
≥3200
≥210
≥1.5
0.167
300
Best Unidirectional Carbon Fiber Fabric

Fabric Type
12K unidirectional carbon fiber fabric
Material
100% carbon fiber
Reinforcement Yarn
Grade I
Tensile Strength(MPa)
≥3500
Tensile Modulus(GPa)
≥240
Elongation(%)
≥1.7
Width(mm)
500
Thickness(mm)
0.167
Weight(g/m2)
300
Bending Strength(MPa)
≥700
Interlaminar shear strength(MPa)
≥45
Storage condition
store dry at 40°-95° F(4° -35°)
Shelf life
10 years
Superiority
1. The texture is soft and light weight, can be effectively applied to uneven surfaces and various harsh shapes.

2. Superior physical properties, tensile strength far exceeds ordinary steel, modulus is better than it.

3.No need for large construction equipment and on-site fixed facilities, the products can be cut freely, with simple construction and short cycle.

4.Green environmental protection is not polluted.


Penggunaan produk
Prompt hangat:

Serat karbon harus disimpan di lingkungan yang sejuk dan kering untuk menghindari sinar matahari

1. Produk itu mudah untuk menghasilkan rambut dan benang, jika Anda menyentuh kulit, itu akan menyebabkan iritasi dan gatal. Jika dihirup,

itu akan menyebabkan kerusakan pada tenggorokan dan paru -paru. Karena produk ini konduktif, jika bersentuhan dengan catu daya, itu mungkin mendapatkan sengatan listrik. Jika berbulu dan serat di udara melekat pada soket, dapat menyebabkan a sirkuit pendek atau menyebabkan
alat untuk bertepuk tangan.

2. Silakan mengatur peralatan pembuangan lokal di tempat kerja, cermin pelindung, sarung tangan pelindung, alat tahan debu harus disertakan dalam pekerjaan. Cash dengan sabun air setelah kontak dengan kulit, cobalah untuk tidak membiarkan bulu dan benang menempel di soket, Dan jangan menyentuh produk dengan catu daya.

3. Limbah dan debu mustard produk ini tidak dapat dibakar. Jika pembakaran akan menyebabkan tungku tidak berfungsi. Diproduksi selama proses pembakaran, fly-ash akan terbang di atmosfer, ada risiko kegagalan listrik, harap dimakamkan dalam limbah industri.
Pengepakan & Pengiriman


Rumah> Produk> Kain serat karbon> Kain serat karbon searah> T700 12K kain serat karbon 300g searah
Kirim permintaan
*
*

We will contact you immediately

Fill in more information so that we can get in touch with you faster

Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.

Kirim